Origin of Optoelectronic Contradictions in 3,4-Cycloalkyl[c]-chalcogenophenes: A Computational Study

The planar morphology of the backbone significantly contributes to the subtle optoelectronic features of π-conjugated polymers. On the other hand, the atomistic tuning of an otherwise identical π-backbone could also impact optoelectronic properties systematically. In this manuscript, we compare a series of 3,4-cycloalkylchalcogenophenes by tuning them atomistically using group-16 elements. Additionally, the effect of systematically extending these building blocks in the form of oligomers and polymers is studied. The size of the 3,4-substitution affected the morphology of the oligomers. In addition, the heteroatoms contributed to a further alteration in their geometry and resultant optoelectronic properties. The chalcogenophenes, containing smaller 3,4-cycloalkanes, resulted in lower bandgap oligomers or polymers compared to those with larger 3,4-cycloalkanes. Natural bonding orbital (NBO) calculations were performed to understand the disparity alongside the contour maps of frontier molecular orbitals (FMO).

The synthesis of such 3,4-cycloalkane-fused chalcogenophenes was explored by Fagan et al. [33] and was later followed by Tilley et al. [34].Rivard et al. extended this technique to make such systems contain Te [35,36].In this context, Zade et al. extensively synthesized CPS-and CPSe-based building blocks, polymers, and copolymers [29,31].CPS and CPSe are among the building blocks, when polymerized or copolymerized, that produce materials showing a decent-to-excellent charge transport [37,38], electrochromic switching, or which complete the red-green-blue color wheel [39].While most CPS-based polymers were found to be amorphous, copolymers based on CPS and bithiazole building blocks showed superior p-type hole mobility arising from the semicrystalline nature of the polymers [37].In parallel to this, 3,4-cyclopenta[c]chalcogenophene(CPX)-and 3,4-cyclohexa[c]chalcogenophene (CHX)-based polymers were also synthesized by Rivard et al. (Figure 1) [40].The cyclohexa[c]tellurophene-and 3-hexylthiophene-based copolymer showed a much higher optical bandgap than the butadiene-and 3-hexylthiophene-based polymer.This indicates that in this polymer, the effect of the heavy atom in lowering the optical bandgap could be overshadowed by the interrupted delocalization of -electrons caused by the steric effect of 3,4-cyclohexyl substitution on the chalcogenophenes.On the other hand, in all CPS-based polymers synthesized by our group, we found a low bandgap.However, the structure of polymer backbones there has been markedly different, leaving no scope for a direct structure-property correlation between the polymers based on CPXs and CHXs.To our surprise, no study exists to compare them from only an atomistic perspective, either experimentally or computationally.To observe the atomistic effect on a chromophore toward its optoelectronic properties, chalcogen atoms were chosen as a successful handle [14,[40][41][42][43][44].An alteration in group-16 elements in the backbone of π-conjugated systems provided versatile tools to achieve diverse prospects [45,46].In addition to the optoelectronic properties, the solidstate packing was influenced heavily by altering the chalcogens, resulting in differential properties in relevant applications [47,48].PCPT and PCPS were synthesized electrochemically and compared with their optoelectronic and spectroelectrochemical properties [29,31].However, the origin of typical optoelectronic features in those with an increasing chain length was never achieved synthetically or computationally from their monomer stage to the polymers via shorter oligomers.Additionally, the furan analog for both CPXs and CHXs was never achieved experimentally.This inspired us to computationally investigate these two research problems in one attempt.First, we investigated the effect of systematically tuning the heteroatoms in CPXs and CHXs (where X = O, S, Se, and Te) and their oligomers, which are nCPXs and nCHXs (n = 2-6) and polymers (CPX)n and (CHX)n.Finally, these broader variations of structures provided us with a comparative correlation between their optoelectronic properties and π-delocalization patterns.To observe the atomistic effect on a chromophore toward its optoelectronic properties, chalcogen atoms were chosen as a successful handle [14,[40][41][42][43][44].An alteration in group-16 elements in the backbone of π-conjugated systems provided versatile tools to achieve diverse prospects [45,46].In addition to the optoelectronic properties, the solid-state packing was influenced heavily by altering the chalcogens, resulting in differential properties in relevant applications [47,48].PCPT and PCPS were synthesized electrochemically and compared with their optoelectronic and spectroelectrochemical properties [29,31].However, the origin of typical optoelectronic features in those with an increasing chain length was never achieved synthetically or computationally from their monomer stage to the polymers via shorter oligomers.Additionally, the furan analog for both CPXs and CHXs was never achieved experimentally.This inspired us to computationally investigate these two research problems in one attempt.First, we investigated the effect of systematically tuning the heteroatoms in CPXs and CHXs (where X = O, S, Se, and Te) and their oligomers, which are nCPXs and nCHXs (n = 2-6) and polymers (CPX) n and (CHX) n .Finally, these broader variations of structures provided us with a comparative correlation between their optoelectronic properties and π-delocalization patterns.

Computational Methodology
All calculations were performed using the density functional theory (DFT) and the Gaussian 16 program package [50].A computational investigation of the effect of the heteroatom on the optoelectronic properties of the parent and 3,4-cycloalkylchalocogenophenes was performed using the density functional theory (DFT) based on the hybrid function of three parameters Becke-3-Lee-Yang-Parr (B3LYP) [51,52] with an SDD pseudopotential basis set [53][54][55].Our group extensively analyzed the structure-property relationship of CPT-or CPS-based systems using functional B3LYP alongside 6-31G(d) as the basis set [29,37].A computational calculation on chalocogenophene-based small molecules or oligomers is quite reliably correlated to their optoelectronic properties using the DFT-B3LYP-6-31G(d) level for smaller chalcogens [56][57][58].However, we anticipated a lack of accuracy in finding a potential energy minimum using a 6-31G(d) basis set for the heavier atoms based on several earlier reports [59][60][61].So, the choice of SDD was made as this effective core potential basis set is known to be useful in circumventing and describing relativistic effects in deep core electrons [62].Thus, SDD reduced the computational cost and presented reliable optimized geometry and energies of the FMO in our calculations.The computationally obtained gas-phase structure and the crystal structure, derived using the XRD method, for (5,5-bis(methoxymethyl)-5,6-dihydro-4H-cyclopenta[c]thiophene-1,3-diyl)bis(trimethylsilane) served as a reference point for the choice of our level of calculation.Therefore, to compare the results in a systematic manner, the basis set (SDD) and functional (B3LYP) were kept identical in all calculations for systems containing different heteroatoms.Notably, the head-tail arrangement in nCPXs or nCHXs was considered for optimization as it is attributed to higher stability compared to head-head-combined oligomers or polymers [32,63].The polymers were optimized under the same program package and identical level of theory with an extension of the periodic boundary condition (PBC) [64,65], which was applied to the unit cell constructed on the optimized geometry of the 2CHX and 2CPXs.Time-dependent DFT (TDDFT) calculations were performed to understand the electronic transitions in nCHXs and nCPXs.The monomers and dimers were calculated for 20 independent electronic transitions, whereas this number was 35 for higher oligomers.Natural bonding orbital (NBO) calculations were performed to understand the electron delocalization pathways in the molecules, respectively.

Crystal Structure
Finding a general computational method to establish an intuitive structure-property relationship in a series of molecules could be challenging and erroneous without experimental support [66].In our previous attempts, the characterization of the solidstate geometry of 5,5-bis(methoxymethyl)-5,6-dihydro-4H-cyclopenta[c]thiophene was unsuccessful.Also, we strongly anticipate that this compound could afford several intermolecular interactions resulting in large packing forces in the solid state, which could, in turn, produce a substantial difference with gas-phase-optimized geometry.So, we planned to characterize (5,5-bis(methoxymethyl)-5,6-dihydro-4H-cyclopenta[c]thioph-ene-1,3-diyl)bis(trimethylsilane), which could afford less π•••π stacking due to the presence of two sterically demanding trimethylsilyl groups on the 2,5-positions of the thiophene ring (Figure 2).The compound was synthesized according to the previously reported method [29] and was recrystallized from heptane as white needles using the slow evaporation method.The crystal structure was unambiguously characterized using the singlecrystal X-ray diffraction (SCXRD) method for the first time.The compound was crystallized in a triclininc space group (P-1), where the unit cell was composed of two molecules bonded to each other through van der Waals forces (O•••H = 2.08 Å).
we planned to characterize (5,5-bis(methoxymethyl)-5,6-dihydro-4Hcyclopenta[c]thioph-ene-1,3-diyl)bis(trimethylsilane), which could afford less  stacking due to the presence of two sterically demanding trimethylsilyl groups on the 2,5positions of the thiophene ring (Figure 2).The compound was synthesized according to the previously reported method [29] and was recrystallized from heptane as white needles using the slow evaporation method.The crystal structure was unambiguously characterized using the single-crystal X-ray diffraction (SCXRD) method for the first time.The compound was crystallized in a triclininc space group (P-1), where the unit cell was composed of two molecules bonded to each other through van der Waals forces (OH = 2.08 Å).In the crystal, the bond angle ∠C1-S3-C4 was 95.4, whereas, in the optimized (DFT-B3LYP-SDD) structure, it is 92.5.The difference in bond length between the solid state and gas-phase-optimized geometry is within a difference of 0.02 Å.These negligible alterations in the gas-phase-optimized structure from solid-state geometry further established the choice of DFT-B3LYP-SDD as the method for computational calculation on such molecules.

Gas-Phase Morphology
The planarity of the heterocycles was an eminent feature in both CPXs and CHXs, which is similar to what has been found earlier in the literature.Interestingly, their oligomers displayed different features in optimized geometry.nCPXs ranging from the monomer to the hexamer exhibited a planarity of -conjugated backbone, which is expected for electronic applications where a delocalized planar -conjugated core effectively influences the optoelectronic properties.By contrast, CHXs showed anomalous morphology upon oligomerization.Unlike CPXs, CHXs exhibited a large dihedral angle between the heterocyclic cores in their gas-phase-optimized structures.This could be attributed to the steric factors of 3,4-cyclohexyl substitution on the chalcogenophene rings.Contextually, PEDOT and PEDOS with a 3,4-ethylenedioxy substitution on chalcogenophene were reported to be planar [30].This concludes that the extra methylene between the CPXs and CHXs is exclusively the reason behind the non-planarity of nCHXs or PCHX.
The heteroatoms also play an important role in the alteration of the geometry within the CHX series.For example, in nCHOs, the noticeable non-planarity of the chains originates at the tetramer (4CHO) stage (Table 1), whereas 2CHS is already substantially nonplanar (Table S4).nCHSe and nCHTe follow a similar trend (Tables S5 and S6) of affording non-planar morphology at an early stage of oligomerization.Additionally, the change in In the crystal, the bond angle ∠C1-S3-C4 was 95.4 • , whereas, in the optimized (DFT-B3LYP-SDD) structure, it is 92.5 • .The difference in bond length between the solid state and gas-phase-optimized geometry is within a difference of 0.02 Å.These negligible alterations in the gas-phase-optimized structure from solid-state geometry further established the choice of DFT-B3LYP-SDD as the method for computational calculation on such molecules.

Gas-Phase Morphology
The planarity of the heterocycles was an eminent feature in both CPXs and CHXs, which is similar to what has been found earlier in the literature.Interestingly, their oligomers displayed different features in optimized geometry.nCPXs ranging from the monomer to the hexamer exhibited a planarity of π-conjugated backbone, which is expected for electronic applications where a delocalized planar π-conjugated core effectively influences the optoelectronic properties.By contrast, CHXs showed anomalous morphology upon oligomerization.Unlike CPXs, CHXs exhibited a large dihedral angle between the heterocyclic cores in their gas-phase-optimized structures.This could be attributed to the steric factors of 3,4-cyclohexyl substitution on the chalcogenophene rings.Contextually, PEDOT and PEDOS with a 3,4-ethylenedioxy substitution on chalcogenophene were reported to be planar [30].This concludes that the extra methylene between the CPXs and CHXs is exclusively the reason behind the non-planarity of nCHXs or PCHX.
The heteroatoms also play an important role in the alteration of the geometry within the CHX series.For example, in nCHOs, the noticeable non-planarity of the chains originates at the tetramer (4CHO) stage (Table 1), whereas 2CHS is already substantially nonplanar (Table S4).nCHSe and nCHTe follow a similar trend (Tables S5 and S6) of affording non-planar morphology at an early stage of oligomerization.Additionally, the change in heteroatoms manifests its effect on the extent of the biaryl twist between chalcogenophene rings.For example, the average biaryl twist angles are 153.4• , 132.9 • , 119.5 • , and 95.3 • for 4CHO, 4CHS, 4CHSe, and 4CHTe, respectively.On the contrary, the biaryl dihedral angle Polymers 2023, 15, 4240 5 of 13 remained unaltered at 180 • for 4CPO, 4CPS, 4CPSe, and 4CPTe.Therefore, the increased volume of the chalcogenophene rings for larger chalcogen atoms is constantly adjusted within the overall framework of the nCPXs, whereas it adds to the already existing steric effect of nCHXs.Notably, there was no remarkable increase in the dihedral angle upon the further extension of the 4CHO oligomer in that series.A similar saturation of the biaryl twist was observed after 2CHS, 2CHSe, and 2CHTe in their corresponding oligomer series.heteroatoms manifests its effect on the extent of the biaryl twist between chalcogenophene rings.For example, the average biaryl twist angles are 153.4,132.9, 119.5, and 95.3 for 4CHO, 4CHS, 4CHSe, and 4CHTe, respectively.On the contrary, the biaryl dihedral angle remained unaltered at 180 for 4CPO, 4CPS, 4CPSe, and 4CPTe.Therefore, the increased volume of the chalcogenophene rings for larger chalcogen atoms is constantly adjusted within the overall framework of the nCPXs, whereas it adds to the already existing steric effect of nCHXs.Notably, there was no remarkable increase in the dihedral angle upon the further extension of the 4CHO oligomer in that series.A similar saturation of the biaryl twist was observed after 2CHS, 2CHSe, and 2CHTe in their corresponding oligomer series.

Optoelectronic Properties
To achieve a structure-optoelectronic property relationship between the series of nCPXs and nCHXs with variable morphological properties, TDDFT calculations were performed under the identical level of calculation, which was used for optimization.The shorter wavelength band in the UV-vis spectra of such molecules is known to arise from several different electronic transitions, whereas the longer band transition is known to be dominated by clear HOMO → LUMO transitions (Figures S7-S20).Therefore, we focused on the longer wavelength transition for a meaningful investigation and unambiguous discussion.However, the complete UV-vis spectra can be found in (Figures S1-S4).The negligible electronic contribution of the aliphatic cyclic 3,4-substitution on the  → * of chalcogenophene was concluded from the UV-vis spectra (Figures 3-6), which showed a small bathochromic shift for mono-CPXs and mono-CHXs compared to their parent chalcogenophenes (furan, thiophene, selenophene, and tellurophene).heteroatoms manifests its effect on the extent of the biaryl twist between chalcogenophene rings.For example, the average biaryl twist angles are 153.4,132.9, 119.5, and 95.3 for 4CHO, 4CHS, 4CHSe, and 4CHTe, respectively.On the contrary, the biaryl dihedral angle remained unaltered at 180 for 4CPO, 4CPS, 4CPSe, and 4CPTe.Therefore, the increased volume of the chalcogenophene rings for larger chalcogen atoms is constantly adjusted within the overall framework of the nCPXs, whereas it adds to the already existing steric effect of nCHXs.Notably, there was no remarkable increase in the dihedral angle upon the further extension of the 4CHO oligomer in that series.A similar saturation of the biaryl twist was observed after 2CHS, 2CHSe, and 2CHTe in their corresponding oligomer series.

Optoelectronic Properties
To achieve a structure-optoelectronic property relationship between the series of nCPXs and nCHXs with variable morphological properties, TDDFT calculations were performed under the identical level of calculation, which was used for optimization.The shorter wavelength band in the UV-vis spectra of such molecules is known to arise from several different electronic transitions, whereas the longer band transition is known to be dominated by clear HOMO → LUMO transitions (Figures S7-S20).Therefore, we focused on the longer wavelength transition for a meaningful investigation and unambiguous discussion.However, the complete UV-vis spectra can be found in (Figures S1-S4).The negligible electronic contribution of the aliphatic cyclic 3,4-substitution on the  → * of chalcogenophene was concluded from the UV-vis spectra (Figures 3-6), which showed a small bathochromic shift for mono-CPXs and mono-CHXs compared to their parent chalcogenophenes (furan, thiophene, selenophene, and tellurophene).heteroatoms manifests its effect on the extent of the biaryl twist between chalcogenophene rings.For example, the average biaryl twist angles are 153.4,132.9, 119.5, and 95.3 for 4CHO, 4CHS, 4CHSe, and 4CHTe, respectively.On the contrary, the biaryl dihedral angle remained unaltered at 180 for 4CPO, 4CPS, 4CPSe, and 4CPTe.Therefore, the increased volume of the chalcogenophene rings for larger chalcogen atoms is constantly adjusted within the overall framework of the nCPXs, whereas it adds to the already existing steric effect of nCHXs.Notably, there was no remarkable increase in the dihedral angle upon the further extension of the 4CHO oligomer in that series.A similar saturation of the biaryl twist was observed after 2CHS, 2CHSe, and 2CHTe in their corresponding oligomer series.

Optoelectronic Properties
To achieve a structure-optoelectronic property relationship between the series of nCPXs and nCHXs with variable morphological properties, TDDFT calculations were performed under the identical level of calculation, which was used for optimization.The shorter wavelength band in the UV-vis spectra of such molecules is known to arise from several different electronic transitions, whereas the longer band transition is known to be dominated by clear HOMO → LUMO transitions (Figures S7-S20).Therefore, we focused on the longer wavelength transition for a meaningful investigation and unambiguous discussion.However, the complete UV-vis spectra can be found in (Figures S1-S4).The negligible electronic contribution of the aliphatic cyclic 3,4-substitution on the  → * of chalcogenophene was concluded from the UV-vis spectra (Figures 3-6), which showed a small bathochromic shift for mono-CPXs and mono-CHXs compared to their parent chalcogenophenes (furan, thiophene, selenophene, and tellurophene).heteroatoms manifests its effect on the extent of the biaryl twist between chalcogenophene rings.For example, the average biaryl twist angles are 153.4,132.9, 119.5, and 95.3 for 4CHO, 4CHS, 4CHSe, and 4CHTe, respectively.On the contrary, the biaryl dihedral angle remained unaltered at 180 for 4CPO, 4CPS, 4CPSe, and 4CPTe.Therefore, the increased volume of the chalcogenophene rings for larger chalcogen atoms is constantly adjusted within the overall framework of the nCPXs, whereas it adds to the already existing steric effect of nCHXs.Notably, there was no remarkable increase in the dihedral angle upon the further extension of the 4CHO oligomer in that series.A similar saturation of the biaryl twist was observed after 2CHS, 2CHSe, and 2CHTe in their corresponding oligomer series.

Optoelectronic Properties
To achieve a structure-optoelectronic property relationship between the series of nCPXs and nCHXs with variable morphological properties, TDDFT calculations were performed under the identical level of calculation, which was used for optimization.The shorter wavelength band in the UV-vis spectra of such molecules is known to arise from several different electronic transitions, whereas the longer band transition is known to be dominated by clear HOMO → LUMO transitions (Figures S7-S20).Therefore, we focused on the longer wavelength transition for a meaningful investigation and unambiguous discussion.However, the complete UV-vis spectra can be found in (Figures S1-S4).The negligible electronic contribution of the aliphatic cyclic 3,4-substitution on the  → * of chalcogenophene was concluded from the UV-vis spectra (Figures 3-6), which showed a small bathochromic shift for mono-CPXs and mono-CHXs compared to their parent chalcogenophenes (furan, thiophene, selenophene, and tellurophene).heteroatoms manifests its effect on the extent of the biaryl twist between chalcogenophene rings.For example, the average biaryl twist angles are 153.4,132.9, 119.5, and 95.3 for 4CHO, 4CHS, 4CHSe, and 4CHTe, respectively.On the contrary, the biaryl dihedral angle remained unaltered at 180 for 4CPO, 4CPS, 4CPSe, and 4CPTe.Therefore, the increased volume of the chalcogenophene rings for larger chalcogen atoms is constantly adjusted within the overall framework of the nCPXs, whereas it adds to the already existing steric effect of nCHXs.Notably, there was no remarkable increase in the dihedral angle upon the further extension of the 4CHO oligomer in that series.A similar saturation of the biaryl twist was observed after 2CHS, 2CHSe, and 2CHTe in their corresponding oligomer series.

Optoelectronic Properties
To achieve a structure-optoelectronic property relationship between the series of nCPXs and nCHXs with variable morphological properties, TDDFT calculations were performed under the identical level of calculation, which was used for optimization.The shorter wavelength band in the UV-vis spectra of such molecules is known to arise from several different electronic transitions, whereas the longer band transition is known to be dominated by clear HOMO → LUMO transitions (Figures S7-S20).Therefore, we focused on the longer wavelength transition for a meaningful investigation and unambiguous discussion.However, the complete UV-vis spectra can be found in (Figures S1-S4).The negligible electronic contribution of the aliphatic cyclic 3,4-substitution on the  → * of chalcogenophene was concluded from the UV-vis spectra (Figures 3-6), which showed a small bathochromic shift for mono-CPXs and mono-CHXs compared to their parent chalcogenophenes (furan, thiophene, selenophene, and tellurophene).heteroatoms manifests its effect on the extent of the biaryl twist between chalcogenophene rings.For example, the average biaryl twist angles are 153.4,132.9, 119.5, and 95.3 for 4CHO, 4CHS, 4CHSe, and 4CHTe, respectively.On the contrary, the biaryl dihedral angle remained unaltered at 180 for 4CPO, 4CPS, 4CPSe, and 4CPTe.Therefore, the increased volume of the chalcogenophene rings for larger chalcogen atoms is constantly adjusted within the overall framework of the nCPXs, whereas it adds to the already existing steric effect of nCHXs.Notably, there was no remarkable increase in the dihedral angle upon the further extension of the 4CHO oligomer in that series.A similar saturation of the biaryl twist was observed after 2CHS, 2CHSe, and 2CHTe in their corresponding oligomer series.

Optoelectronic Properties
To achieve a structure-optoelectronic property relationship between the series of nCPXs and nCHXs with variable morphological properties, TDDFT calculations were performed under the identical level of calculation, which was used for optimization.The shorter wavelength band in the UV-vis spectra of such molecules is known to arise from several different electronic transitions, whereas the longer band transition is known to be dominated by clear HOMO → LUMO transitions (Figures S7-S20).Therefore, we focused on the longer wavelength transition for a meaningful investigation and unambiguous discussion.However, the complete UV-vis spectra can be found in (Figures S1-S4).The negligible electronic contribution of the aliphatic cyclic 3,4-substitution on the  → * of chalcogenophene was concluded from the UV-vis spectra (Figures 3-6), which showed a small bathochromic shift for mono-CPXs and mono-CHXs compared to their parent chalcogenophenes (furan, thiophene, selenophene, and tellurophene).heteroatoms manifests its effect on the extent of the biaryl twist between chalcogenophene rings.For example, the average biaryl twist angles are 153.4,132.9, 119.5, and 95.3 for 4CHO, 4CHS, 4CHSe, and 4CHTe, respectively.On the contrary, the biaryl dihedral angle remained unaltered at 180 for 4CPO, 4CPS, 4CPSe, and 4CPTe.Therefore, the increased volume of the chalcogenophene rings for larger chalcogen atoms is constantly adjusted within the overall framework of the nCPXs, whereas it adds to the already existing steric effect of nCHXs.Notably, there was no remarkable increase in the dihedral angle upon the further extension of the 4CHO oligomer in that series.A similar saturation of the biaryl twist was observed after 2CHS, 2CHSe, and 2CHTe in their corresponding oligomer series.

Optoelectronic Properties
To achieve a structure-optoelectronic property relationship between the series of nCPXs and nCHXs with variable morphological properties, TDDFT calculations were performed under the identical level of calculation, which was used for optimization.The shorter wavelength band in the UV-vis spectra of such molecules is known to arise from several different electronic transitions, whereas the longer band transition is known to be dominated by clear HOMO → LUMO transitions (Figures S7-S20).Therefore, we focused on the longer wavelength transition for a meaningful investigation and unambiguous discussion.However, the complete UV-vis spectra can be found in (Figures S1-S4).The negligible electronic contribution of the aliphatic cyclic 3,4-substitution on the  → * of chalcogenophene was concluded from the UV-vis spectra (Figures 3-6), which showed a small bathochromic shift for mono-CPXs and mono-CHXs compared to their parent chalcogenophenes (furan, thiophene, selenophene, and tellurophene).heteroatoms manifests its effect on the extent of the biaryl twist between chalcogenophene rings.For example, the average biaryl twist angles are 153.4,132.9, 119.5, and 95.3 for 4CHO, 4CHS, 4CHSe, and 4CHTe, respectively.On the contrary, the biaryl dihedral angle remained unaltered at 180 for 4CPO, 4CPS, 4CPSe, and 4CPTe.Therefore, the increased volume of the chalcogenophene rings for larger chalcogen atoms is constantly adjusted within the overall framework of the nCPXs, whereas it adds to the already existing steric effect of nCHXs.Notably, there was no remarkable increase in the dihedral angle upon the further extension of the 4CHO oligomer in that series.A similar saturation of the biaryl twist was observed after 2CHS, 2CHSe, and 2CHTe in their corresponding oligomer series.

Optoelectronic Properties
To achieve a structure-optoelectronic property relationship between the series of nCPXs and nCHXs with variable morphological properties, TDDFT calculations were performed under the identical level of calculation, which was used for optimization.The shorter wavelength band in the UV-vis spectra of such molecules is known to arise from several different electronic transitions, whereas the longer band transition is known to be dominated by clear HOMO → LUMO transitions (Figures S7-S20).Therefore, we focused on the longer wavelength transition for a meaningful investigation and unambiguous discussion.However, the complete UV-vis spectra can be found in (Figures S1-S4).The negligible electronic contribution of the aliphatic cyclic 3,4-substitution on the  → * of chalcogenophene was concluded from the UV-vis spectra (Figures 3-6), which showed a small bathochromic shift for mono-CPXs and mono-CHXs compared to their parent chalcogenophenes (furan, thiophene, selenophene, and tellurophene).heteroatoms manifests its effect on the extent of the biaryl twist between chalcogenophene rings.For example, the average biaryl twist angles are 153.4,132.9, 119.5, and 95.3 for 4CHO, 4CHS, 4CHSe, and 4CHTe, respectively.On the contrary, the biaryl dihedral angle remained unaltered at 180 for 4CPO, 4CPS, 4CPSe, and 4CPTe.Therefore, the increased volume of the chalcogenophene rings for larger chalcogen atoms is constantly adjusted within the overall framework of the nCPXs, whereas it adds to the already existing steric effect of nCHXs.Notably, there was no remarkable increase in the dihedral angle upon the further extension of the 4CHO oligomer in that series.A similar saturation of the biaryl twist was observed after 2CHS, 2CHSe, and 2CHTe in their corresponding oligomer series.

Optoelectronic Properties
To achieve a structure-optoelectronic property relationship between the series of nCPXs and nCHXs with variable morphological properties, TDDFT calculations were performed under the identical level of calculation, which was used for optimization.The shorter wavelength band in the UV-vis spectra of such molecules is known to arise from several different electronic transitions, whereas the longer band transition is known to be dominated by clear HOMO → LUMO transitions (Figures S7-S20).Therefore, we focused on the longer wavelength transition for a meaningful investigation and unambiguous discussion.However, the complete UV-vis spectra can be found in (Figures S1-S4).The negligible electronic contribution of the aliphatic cyclic 3,4-substitution on the  → * of chalcogenophene was concluded from the UV-vis spectra (Figures 3-6), which showed a small bathochromic shift for mono-CPXs and mono-CHXs compared to their parent chalcogenophenes (furan, thiophene, selenophene, and tellurophene).heteroatoms manifests its effect on the extent of the biaryl twist between chalcogenophene rings.For example, the average biaryl twist angles are 153.4,132.9, 119.5, and 95.3 for 4CHO, 4CHS, 4CHSe, and 4CHTe, respectively.On the contrary, the biaryl dihedral angle remained unaltered at 180 for 4CPO, 4CPS, 4CPSe, and 4CPTe.Therefore, the increased volume of the chalcogenophene rings for larger chalcogen atoms is constantly adjusted within the overall framework of the nCPXs, whereas it adds to the already existing steric effect of nCHXs.Notably, there was no remarkable increase in the dihedral angle upon the further extension of the 4CHO oligomer in that series.A similar saturation of the biaryl twist was observed after 2CHS, 2CHSe, and 2CHTe in their corresponding oligomer series.

Optoelectronic Properties
To achieve a structure-optoelectronic property relationship between the series of nCPXs and nCHXs with variable morphological properties, TDDFT calculations were performed under the identical level of calculation, which was used for optimization.The shorter wavelength band in the UV-vis spectra of such molecules is known to arise from several different electronic transitions, whereas the longer band transition is known to be dominated by clear HOMO → LUMO transitions (Figures S7-S20).Therefore, we focused on the longer wavelength transition for a meaningful investigation and unambiguous discussion.However, the complete UV-vis spectra can be found in (Figures S1-S4).The negligible electronic contribution of the aliphatic cyclic 3,4-substitution on the  → * of chalcogenophene was concluded from the UV-vis spectra (Figures 3-6), which showed a small bathochromic shift for mono-CPXs and mono-CHXs compared to their parent chalcogenophenes (furan, thiophene, selenophene, and tellurophene).heteroatoms manifests its effect on the extent of the biaryl twist between chalcogenophene rings.For example, the average biaryl twist angles are 153.4,132.9, 119.5, and 95.3 for 4CHO, 4CHS, 4CHSe, and 4CHTe, respectively.On the contrary, the biaryl dihedral angle remained unaltered at 180 for 4CPO, 4CPS, 4CPSe, and 4CPTe.Therefore, the increased volume of the chalcogenophene rings for larger chalcogen atoms is constantly adjusted within the overall framework of the nCPXs, whereas it adds to the already existing steric effect of nCHXs.Notably, there was no remarkable increase in the dihedral angle upon the further extension of the 4CHO oligomer in that series.A similar saturation of the biaryl twist was observed after 2CHS, 2CHSe, and 2CHTe in their corresponding oligomer series.

Optoelectronic Properties
To achieve a structure-optoelectronic property relationship between the series of nCPXs and nCHXs with variable morphological properties, TDDFT calculations were performed under the identical level of calculation, which was used for optimization.The shorter wavelength band in the UV-vis spectra of such molecules is known to arise from several different electronic transitions, whereas the longer band transition is known to be dominated by clear HOMO → LUMO transitions (Figures S7-S20).Therefore, we focused on the longer wavelength transition for a meaningful investigation and unambiguous discussion.However, the complete UV-vis spectra can be found in (Figures S1-S4).The negligible electronic contribution of the aliphatic cyclic 3,4-substitution on the  → * of chalcogenophene was concluded from the UV-vis spectra (Figures 3-6), which showed a small bathochromic shift for mono-CPXs and mono-CHXs compared to their parent chalcogenophenes (furan, thiophene, selenophene, and tellurophene).heteroatoms manifests its effect on the extent of the biaryl twist between chalcogenophene rings.For example, the average biaryl twist angles are 153.4,132.9, 119.5, and 95.3 for 4CHO, 4CHS, 4CHSe, and 4CHTe, respectively.On the contrary, the biaryl dihedral angle remained unaltered at 180 for 4CPO, 4CPS, 4CPSe, and 4CPTe.Therefore, the increased volume of the chalcogenophene rings for larger chalcogen atoms is constantly adjusted within the overall framework of the nCPXs, whereas it adds to the already existing steric effect of nCHXs.Notably, there was no remarkable increase in the dihedral angle upon the further extension of the 4CHO oligomer in that series.A similar saturation of the biaryl twist was observed after 2CHS, 2CHSe, and 2CHTe in their corresponding oligomer series.

Optoelectronic Properties
To achieve a structure-optoelectronic property relationship between the series of nCPXs and nCHXs with variable morphological properties, TDDFT calculations were performed under the identical level of calculation, which was used for optimization.The shorter wavelength band in the UV-vis spectra of such molecules is known to arise from several different electronic transitions, whereas the longer band transition is known to be dominated by clear HOMO → LUMO transitions (Figures S7-S20).Therefore, we focused on the longer wavelength transition for a meaningful investigation and unambiguous discussion.However, the complete UV-vis spectra can be found in (Figures S1-S4).The negligible electronic contribution of the aliphatic cyclic 3,4-substitution on the  → * of chalcogenophene was concluded from the UV-vis spectra (Figures 3-6), which showed a small bathochromic shift for mono-CPXs and mono-CHXs compared to their parent chalcogenophenes (furan, thiophene, selenophene, and tellurophene).

(CHO) n
Polymers 2023, 15, x FOR PEER REVIEW 5 of 14 heteroatoms manifests its effect on the extent of the biaryl twist between chalcogenophene rings.For example, the average biaryl twist angles are 153.4,132.9, 119.5, and 95.3 for 4CHO, 4CHS, 4CHSe, and 4CHTe, respectively.On the contrary, the biaryl dihedral angle remained unaltered at 180 for 4CPO, 4CPS, 4CPSe, and 4CPTe.Therefore, the increased volume of the chalcogenophene rings for larger chalcogen atoms is constantly adjusted within the overall framework of the nCPXs, whereas it adds to the already existing steric effect of nCHXs.Notably, there was no remarkable increase in the dihedral angle upon the further extension of the 4CHO oligomer in that series.A similar saturation of the biaryl twist was observed after 2CHS, 2CHSe, and 2CHTe in their corresponding oligomer series.

Optoelectronic Properties
To achieve a structure-optoelectronic property relationship between the series of nCPXs and nCHXs with variable morphological properties, TDDFT calculations were performed under the identical level of calculation, which was used for optimization.The shorter wavelength band in the UV-vis spectra of such molecules is known to arise from several different electronic transitions, whereas the longer band transition is known to be dominated by clear HOMO → LUMO transitions (Figures S7-S20).Therefore, we focused on the longer wavelength transition for a meaningful investigation and unambiguous discussion.However, the complete UV-vis spectra can be found in (Figures S1-S4).The negligible electronic contribution of the aliphatic cyclic 3,4-substitution on the  → * of chalcogenophene was concluded from the UV-vis spectra (Figures 3-6), which showed a small bathochromic shift for mono-CPXs and mono-CHXs compared to their parent chalcogenophenes (furan, thiophene, selenophene, and tellurophene).

(CPO) n
Polymers 2023, 15, x FOR PEER REVIEW 5 of 14 heteroatoms manifests its effect on the extent of the biaryl twist between chalcogenophene rings.For example, the average biaryl twist angles are 153.4,132.9, 119.5, and 95.3 for 4CHO, 4CHS, 4CHSe, and 4CHTe, respectively.On the contrary, the biaryl dihedral angle remained unaltered at 180 for 4CPO, 4CPS, 4CPSe, and 4CPTe.Therefore, the increased volume of the chalcogenophene rings for larger chalcogen atoms is constantly adjusted within the overall framework of the nCPXs, whereas it adds to the already existing steric effect of nCHXs.Notably, there was no remarkable increase in the dihedral angle upon the further extension of the 4CHO oligomer in that series.A similar saturation of the biaryl twist was observed after 2CHS, 2CHSe, and 2CHTe in their corresponding oligomer series.

Optoelectronic Properties
To achieve a structure-optoelectronic property relationship between the series of nCPXs and nCHXs with variable morphological properties, TDDFT calculations were performed under the identical level of calculation, which was used for optimization.The shorter wavelength band in the UV-vis spectra of such molecules is known to arise from several different electronic transitions, whereas the longer band transition is known to be dominated by clear HOMO → LUMO transitions (Figures S7-S20).Therefore, we focused on the longer wavelength transition for a meaningful investigation and unambiguous discussion.However, the complete UV-vis spectra can be found in (Figures S1-S4).The negligible electronic contribution of the aliphatic cyclic 3,4-substitution on the  → * of chalcogenophene was concluded from the UV-vis spectra (Figures 3-6), which showed a small bathochromic shift for mono-CPXs and mono-CHXs compared to their parent chalcogenophenes (furan, thiophene, selenophene, and tellurophene).

Optoelectronic Properties
To achieve a structure-optoelectronic property relationship between the series of nCPXs and nCHXs with variable morphological properties, TDDFT calculations were performed under the identical level of calculation, which was used for optimization.The shorter wavelength band in the UV-vis spectra of such molecules is known to arise from several different electronic transitions, whereas the longer band transition is known to be dominated by clear HOMO → LUMO transitions (Figures S7-S20).Therefore, we focused on the longer wavelength transition for a meaningful investigation and unambiguous discussion.However, the complete UV-vis spectra can be found in (Figures S1-S4).The negligible electronic contribution of the aliphatic cyclic 3,4-substitution on the π → π* of chalcogenophene was concluded from the UV-vis spectra (Figures 3-6), which showed a small bathochromic shift for mono-CPXs and mono-CHXs compared to their parent chalcogenophenes (furan, thiophene, selenophene, and tellurophene).
The CPX and CHX monomers showed a distinct π → π* transition in the almost similar position of spectra (Figure 6).However, the extension of CPX and CHX building blocks to nCPXs and nCHXs brings remarkable differences.In the nCPX series, an increase in the length of oligomers in any series of chalcogenophenes showed a similar trend for the bathochromic shift (Figure 7).For example, the wavelength of absorption maxima (λ max ) increased from 205 nm for CPO to 497 nm for 6CPO (Figure 7a).This was identical to the extension of the parent furan molecule.nCHXs also showed similar features of a continuous bathochromic shift to a similar extent via elongation compared to nCPO or parent furan series (Figure 7b).A remarkable change was observed in the case of the thiophene series.After an almost similar bathochromic shift for the π → π* transition at the dimer stage, the deviation of 3CHS was discernible compared to the terthiophene or 3CPS.In the selenophene series, λ max for nCPSes deviated almost negligibly (~5 nm) compared to the oligoselenophenes of similar length, whereas nCHSes deviated from the rest of the congeners at even the dimer stage by 26 nm (Figure 7c).Upon further elongation, the difference between λ max for the nCHSes became prominent compared to nCPSes or oligoselenophenes of the same length, leading to a saturation in the optical bandgap beyond 4CHSe.In the tellurophene series, 2CHTe displayed a substantially low increase in λ max compared to parent bitellurophene and 2CPTe, which upon further elongation of the chain length, could not yield any conspicuous changes (Figure 7d).The phenomena of an extension of a π-conjugated building block and an increase in the λ max of the π → π* transition are generally attributed to the extended delocalization of the π-electron system, which converges the HOMO-LUMO gap into a narrower range.However, we found that an increase in n for nCHXs is contradictory to it.This could be due to the lack of π-conjugation, which is triggered by a lack of planar geometry in the higher oligomers compared to those of nCPXs or the parent chalcogenophenes of a similar chain length.In CHXs, the presence of one extra methylene group, compared to CPXs, affects the morphology of the polymer chain, impacting effective π-delocalization.On top of that, upon exchanging the heteroatom in the oligomers with the heavier group-16 elements, the already non-planar oligomers further deviated from a suitable geometry for an effective π-overlap of the orbitals toward delocalization.The contour plots of frontier molecular orbitals (FMOs) were compared between 2CHS and 2CPS to identify a subtle difference in electron delocalization in both molecules (Figure 8a-d).The covalent bond connecting these two chalcogenophene rings showed a twisted nature of electron density around the connecting bond.This is a clear indication of a disruption in the extension of π-conjugation in the 2CHS molecule, where the overlapping lobes of p-orbitals move away from each other to a similar extent but in opposite directions.The CPX and CHX monomers showed a distinct  → * transition in the almost similar position of spectra (Figure 6).However, the extension of CPX and CHX building blocks to nCPXs and nCHXs brings remarkable differences.In the nCPX series, an increase in the length of oligomers in any series of chalcogenophenes showed a similar trend for the bathochromic shift (Figure 7).For example, the wavelength of absorption maxima (max) increased from 205 nm for CPO to 497 nm for 6CPO (Figure 7a).This was identical to the extension of the parent furan molecule.nCHXs also showed similar features of a continuous bathochromic shift to a similar extent via elongation compared to nCPO or parent furan series (Figure 7b).A remarkable change was observed in the case of the thi- NBO calculations performed on 2CHT and 2CPT provided a clear insight into the lack of electron delocalization between the two rings through the increased dihedral angle.In 2CPT (Figure 8e), the charge transfer was found between the bonding orbital of C15-C26 (ED i = 0.6839) and C2-C14 (EDj = 0.7296) with a stabilization energy (E 2 ) of 16.96 kcal/mol) Polymers 2023, 15, 4240 8 of 13 (Figure 8e).Also, C15-C26 (ED i = 0.6839) to C16-C27 (ED j = 0.7315) was identified with an E 2 of 17.47 kcal/mol.These π → π* transitions have a similar stabilization energy of the LP → π* electron transfer as E 2 for LP S29 → where the antibonding NBO of C1-C12 (EDj = 0.7315) is 16.01 kcal/mol.In 2CHS, E 2 for electron transfer from the LP of S36 to the antibonding NBO of C1-C2 (EDj = 0.6772) was 15.86 kcal/mol and that for the electron transfer between C18 and C19 (ED i = 0.7358) to C1-C2 (ED j = 0.6772) was only 1.85 kcal/mol (Figure 8f).However, major stabilization in the molecule was obtained from the electron transfer between C3 and C4 (EDj = 0.6872) to C1-C2 (EDj = 0.6772) with an E 2 of kcal/mol.This explains that the intra-unit and inter-unit electron delocalization in 2CPS equally contributed to the stabilization of the molecule in an identical manner to the delocalization of the lone pair of electrons.However, the intra-ring electron delocalization and delocalized lone pair of electrons were found to be the only energy stabilizing factor in 2CHS, lacking any potential energy stabilization via the inter-unit orbital overlap.This was reciprocated in the typical trend of HOMO-LUMO energies of the oligomers upon increasing the chain length.The phenomena of an extension of a π-conjugated building block and an increase in the max of the  → * transition are generally attributed to the extended delocalization of the -electron system, which converges the HOMO-LUMO gap into a narrower range.However, we found that an increase in n for nCHXs is contradictory to it.This could be due to the lack of -conjugation, which is triggered by a lack of planar geometry in the higher oligomers compared to those of nCPXs or the parent chalcogenophenes of a similar  NBO calculations performed on 2CHT and 2CPT provided a clear insight into the lack of electron delocalization between the two rings through the increased dihedral angle.In 2CPT (Figure 8e), the charge transfer was found between the bonding orbital of C15-C26 (EDi = 0.6839) and C2-C14 (EDj = 0.7296) with a stabilization energy (E 2 ) of 16.96 kcal/mol) (Figure 8e).Also, C15-C26 (EDi = 0.6839) to C16-C27 (EDj = 0.7315) was identified with an E 2 of 17.47 kcal/mol.These  → * have a similar stabilization energy of the LP → * electron transfer as E 2 for LP S29 → where the antibonding NBO of C1-C12 (EDj = 0.7315) is 16.01 kcal/mol.In 2CHS, E 2 for electron transfer from the LP of S36 to the antibonding NBO of C1-C2 (EDj = 0.6772) was 15.86 kcal/mol and that for the electron transfer between C18 and C19 (EDi = 0.7358) to C1-C2 (EDj = 0.6772) was only 1.85 kcal/mol (Figure 8f).However, major stabilization in the molecule was obtained from the electron transfer between C3 and C4 (EDj = 0.6872) to C1-C2 (EDj = 0.6772) with an E 2 of kcal/mol.This explains that the intra-unit and inter-unit electron delocalization in 2CPS equally contributed to the stabilization of the molecule in an identical manner to the delocalization of the lone pair of electrons.However, the intra-ring electron delocalization and delocalized lone pair of electrons were found to be the only energy stabilizing factor in 2CHS, lacking any potential energy stabilization via the inter-unit orbital overlap.This was reciprocated in the typical trend of HOMO-LUMO energies of the oligomers upon increasing the chain length.
The differential trend of energies for FMOs in nCPXs and nCHXs needs to be accounted for from two directions, including the (a) atomistic effect and (b) the effect of chain extension (Figure 9).Notably, the stabilization of the HOMO level from furan to thiophene within a series of oligomers of identical length remained a general trend due to the lower aromatic nature of the furan rings than the other chalcogenophenes.In CHXs, heavier chalcogens stabilized the HOMO in the monomer in a similar manner to the parent chalcogenophenes.However, from the dimer to the polymer, it showed the stabilization of the HOMO due to less conjugation.The LUMO levels of the monomer and parent chalcogenophene were stabilized with the insertion of heavier chalcogens.However, for n ≥ 2, the trends were reversed, resulting in the destabilization of LUMO due to less delocalization.These two antagonistic effects cause an increase in the HOMO-LUMO gap for the nCHX (n ≥ 2) or PCHXs, which further increases upon the insertion of heavier chalcogen atoms.In CPXs, the trend of destabilization of the HOMO originates from both the insertion The differential trend of energies for FMOs in nCPXs and nCHXs needs to be accounted for from two directions, including the (a) atomistic effect and (b) the effect of chain extension (Figure 9).Notably, the stabilization of the HOMO level from furan to thiophene within a series of oligomers of identical length remained a general trend due to the lower aromatic nature of the furan rings than the other chalcogenophenes.In CHXs, heavier chalcogens stabilized the HOMO in the monomer in a similar manner to the parent chalcogenophenes.However, from the dimer to the polymer, it showed the stabilization of the HOMO due to less conjugation.The LUMO levels of the monomer and parent chalcogenophene were stabilized with the insertion of heavier chalcogens.However, for n ≥ 2, the trends were reversed, resulting in the destabilization of LUMO due to less delocalization.These two antagonistic effects cause an increase in the HOMO-LUMO gap for the nCHX (n ≥ 2) or PCHXs, which further increases upon the insertion of heavier chalcogen atoms.In CPXs, the trend of destabilization of the HOMO originates from both the insertion of the heteroatoms and the elongation of the polymer chain.In addition to this, the LUMO levels were stabilized by these factors.These two synergistic effects caused a lowering in the HOMO-LUMO gap in nCPXs (n ≥ 2) or PCPXs.
Polymers 2023, 15, x FOR PEER REVIEW 10 of 14 of the heteroatoms and the elongation of the polymer chain.In addition to this, the LUMO levels were stabilized by these factors.These two synergistic effects caused a lowering in the HOMO-LUMO gap in nCPXs (n ≥ 2) or PCPXs.

Discussion
The systematic comparison between the origin of optoelectronic properties in 3,4cycloalkyl[c]chalcogenophenes was necessary.We did not consider the 3,4-cyclo-

Discussion
The systematic comparison between the origin of optoelectronic properties in 3,4-cycloalkyl[c]chalcogenophenes was necessary.We did not consider the 3,4cyclobuta[c]chalcogenophene for this purpose for two reasons.First, the 3,4-cyclobutane asserts enormous strain on that heteroaromatic ring, which could force the rehybridization of the orbitals in chalcogenophenes.Finally, the 3,4-cyclobuta[c]chalcogenophenes were not synthetically available.However, the CPXs and CHXs proved to be useful designs for understanding several factors that influence the optoelectronic properties of a π-conjugated building block upon the elongation of chain length.Our study complements previous experimental outcomes of low-bandgap polymers from CPS-or CPSe-based systems and high-bandgap polymers from CHX-based systems.Our earlier reports on the synthesis and characterization of poly-CPT support the proof of the concept here as the colorless CPT building block, when electropolymerized, showed yellow-orange oligomers and a blue polymer [29].Also, the excellent electronic properties of polymers arising from planar morphologies were anticipated from our study.Our computational calculation completely supports that observation with a lowering of the bandgap resulting from a higher degree of oligomerization.CPXs were proved to be the preferable building blocks where the resulting copolymers or block copolymers were expected to achieve planar morphology and a lower bandgap via electronic delocalization.The electronic effects based on the donor-acceptor intramolecular charge transfer strategy also anticipated the use of CPX-based π-systems over CHX-based architecture, whereas CHXs could have potential in applications where weakly delocalized covalently bonded π-systems are expected.Block copolymers consisting of CPXs and CHXs as two different building blocks could significantly attain very different morphology and optoelectronic properties compared to the individual homopolymers, which has synthetically not been achieved yet.CPTe carries significant potential in terms of the planar π-conjugated system, phosphorescence [67][68][69], and low bandgap [70][71][72].

Conclusions
We successfully found a path through which optoelectronic contradictions are systematically generated upon an increase in the chain length of covalently bonded CPXs and CHXs.In CHXs, the elongation of the monomer to oligomer and polymer resulted in the planar to twisted morphology of the π-conjugated chain.The optoelectronic properties were affected because of this non-planar morphology and as the HOMO-LUMO gap increased with the extension of the chain length.Heavier heteroatoms further magnified this detrimental effect to result in large bandgap oligomers and polymers.The reason for increasing the disruption in the CHXs was attributed to the lack of delocalization of the π-electrons among the covalently bonded building blocks through the help of NBO calculation and HOMO-LUMO contour maps.On the other hand, the oligomer or polymer chains remained planar despite changes in the number of attached building blocks or the insertion of heavier chalcogen atoms in nCPXs.As a result, the HOMO-LUMO gap kept on decreasing.CPX series showed a remarkable decrease in the HOMO-LUMO gap upon extension.PCPTe was found to possess a wider than that of PCHTe by two times.Interesting features could be introduced in alternate, or block copolymers made of CPX and CHX building blocks.PCPTe holds the potential to construct very low-bandgap polymers and, in terms of its anticipated phosphorescence, could be applied in relevant electronic applications.
and (b) nCPO.Transitions at a shorter wavelength were omitted for data clarity.

Table 1 .
Optimized geometry of the oligomer and polymers of CPO and CHO at the DFT-B3LYP-SDD level of theory.

Table 1 .
Optimized geometry of the oligomer and polymers of CPO and CHO at the DFT-B3LYP-SDD level of theory.

Table 1 .
Optimized geometry of the oligomer and polymers of CPO and CHO at the DFT-B3LYP-SDD level of theory.

Table 1 .
Optimized geometry of the oligomer and polymers of CPO and CHO at the DFT-B3LYP-SDD level of theory.

Table 1 .
Optimized geometry of the oligomer and polymers of CPO and CHO at the DFT-B3LYP-SDD level of theory.

Table 1 .
Optimized geometry of the oligomer and polymers of CPO and CHO at the DFT-B3LYP-SDD level of theory.

Table 1 .
Optimized geometry of the oligomer and polymers of CPO and CHO at the DFT-B3LYP-SDD level of theory.

Table 1 .
Optimized geometry of the oligomer and polymers of CPO and CHO at the DFT-B3LYP-SDD level of theory.

Table 1 .
Optimized geometry of the oligomer and polymers of CPO and CHO at the DFT-B3LYP-SDD level of theory.

Table 1 .
Optimized geometry of the oligomer and polymers of CPO and CHO at the DFT-B3LYP-SDD level of theory.

Table 1 .
Optimized geometry of the oligomer and polymers of CPO and CHO at the DFT-B3LYP-SDD level of theory.

Table 1 .
Optimized geometry of the oligomer and polymers of CPO and CHO at the DFT-B3LYP-SDD level of theory.

Table 1 .
Optimized geometry of the oligomer and polymers of CPO and CHO at the DFT-B3LYP-SDD level of theory.

Table 1 .
Optimized geometry of the oligomer and polymers of CPO and CHO at the DFT-B3LYP-SDD level of theory.

Table 1 .
Optimized geometry of the oligomer and polymers of CPO and CHO at the DFT-B3LYP-SDD level of theory.